Cumque nudaveris patrem • Tittanium Materias et Cellarius: Pura Titanium (CP) titanium offensionibus et ffoyle,Grade1, Gradus II, Gradus V, Gradus V, Gradus Part VII et IX
• Formae: No habena et coil, aut FUSUS. Slitting praesto ministerium
• ratio: Crassitudine: ≥0.01mm: XX ~ 1000mm: Longitudo, ut Request
• condicionibus hominum: Frigus advolvit (V) ~ Hot advolvit (R) Annealed (M) Status Solidum
• Signa: ASTM B265, AMS (IV)CMXI, ams (IV)CMII, ASTM F67, ASTM F136 etc.
• Appilications:Electronics, chemicals, vigilias, specula, jewelry, alludens bona, machinery erunt: et operies apparatu, environmental apparatu, golf et precision machining industries.
Titanium Alloys Material Common Name | ||
Gr1 |
R50250 UNS |
Ti-CP |
Gr2 |
R50400 UNS |
Ti-CP |
Gr4 |
R50700 UNS |
Ti-CP |
Gr7 |
R52400 UNS |
Ti 0.20Pd |
G9 |
R56320 UNS |
Ti-3AL 2.5V |
G11 |
R52250 UNS |
Ti 0.15Pd |
G12 |
R53400 UNS | Ti-0.3Mo 0.8Ni |
G16 |
R52402 UNS | Ti 0.05Pd |
G23 |
R56407 UNS |
4v-ti-6al ELI |
Cumque nudaveris patrem et Titanium Cellarius: Cumque nudaveris patrem maxime provide autem de pura Titanium Magnetic Gr1, Gr2, Gr4 grades; Nam titanium alloy Cellarius: Nos Gr5 maxime provide, Gr7, Gr9, Gr11, Gr12, Gr16, et alia Gr23 grades, et laminam titanium sunt productum est amplius ex in frigore volubilem; Titanium productio processus est magis complicated sheet. Imperium proprie est deformatio potest esse processus in rolling.That magnitudinum secundum mos est scriptor Conscidisti in diversas necessitates, magna dedit, breve reddat tempus.
gradus |
Chemical compositionem, percent pondus (%) |
||||||||||||
C (≤) |
O (≤) |
N (≤) |
H (≤) |
Fe (≤) |
al |
V |
Pd Palladium |
RU |
NI |
Mo. |
alii Elementa Max. quisque |
alii Elementa Max. summa |
|
Gr1 |
0,08 |
0,18 |
0,03 |
0.015 |
0.20 |
— |
— |
— |
— |
— |
— |
0,1 |
0,4 |
Gr2 |
0,08 |
0,25 |
0,03 |
0.015 |
0,30 |
— |
— |
— |
— |
— |
— |
0,1 |
0,4 |
Gr4 |
0,08 |
0,25 |
0,03 |
0.015 |
0,30 |
— |
— |
— |
— |
— |
— |
0,1 |
0,4 |
Gr5 |
0,08 |
0.20 |
0,05 |
0.015 |
0,40 |
5.5 6,75 |
3.5 4.5 |
— |
— |
— |
— |
0,1 |
0,4 |
Gr7 |
0,08 |
0,25 |
0,03 |
0.015 |
0,30 |
— |
— |
0,12 0,25 |
— |
0,12 0,25 |
— |
0,1 |
0,4 |
Gr9 |
0,08 |
0.15 |
0,03 |
0.015 |
0,25 |
2.5 3.5 |
2.0 3.0 |
— |
— |
— |
— |
0,1 |
0,4 |
Gr11 |
0,08 |
0,18 |
0,03 |
0.15 |
0,2 |
— |
— |
0,12 0,25 |
— |
— |
— |
0,1 |
0,4 |
Gr12 |
0,08 |
0,25 |
0,03 |
0.15 |
0,3 |
— |
— |
— |
— |
0,6 0,9 |
0.2 0.4 |
0,1 |
0,4 |
Gr16 |
0,08 |
0,25 |
0,03 |
0.15 |
0,3 |
— |
— |
0,04 0,08 |
— |
— |
— |
0,1 |
0,4 |
Gr23 |
0,08 |
0,13 |
0,03 |
0.125 |
0,25 |
5.5 6.5 |
3.5 4.5 |
— |
— |
— |
— |
0,1 |
0,1 |
gradus |
Spermatophyta |
|||||||
Distrahentes fortitudo min |
Cedat imperium Min (0.2%, offset) |
Per elongationem 4D Sumus (%) |
Reductio onerum Area Sumus (%) |
Subjicite Test (Radius circuli mandrel) |
||||
ksi |
MPa |
ksi |
MPa |
<1.8mm grossum in |
In crassitudine 1.8-4.8mm | |||
Gr1 |
35 |
240 |
20 |
138 |
24 |
30 |
1.5T | 2.0T |
Gr2 |
50 |
345 |
40 |
275 |
20 |
30 |
2.0T | 2.5T |
Gr4 |
80 |
550 |
70 |
483 |
15 |
25 |
2.5T | 3.0T |
Gr5 |
130 |
895 |
120 |
828 |
10 |
25 |
4.5T | 5.0T |
Gr7 |
50 |
345 |
40 |
275 |
20 |
30 |
2.0T | 2.5T |
Gr9 |
90 |
620 |
70 |
483 |
15 |
25 |
2.5T | 3.0T |
Gr11 |
35 |
240 |
20 |
138 |
24 |
30 |
1.5T | 2.0T |
Gr12 |
70 |
483 |
50 |
345 |
18 |
25 |
2.0T | 2.5T |
Gr16 |
50 |
345 |
40 |
275 |
20 |
30 |
2.0T | 2.5T |
Gr23 |
120 |
828 |
110 |
759 |
10 |
15 |
4.5T | 5.0T |
• I gradu, castitatis Titanium modo, secundum quid ductilitas excelsum vires et humilis.
• Gradus II: De pura Titanium Magnetic plurimum usus est. Est optimum compositum de viribus
• Gradus III: High Titanium vires, usus quoad caudas, quia matrix in testa solida, & tubo; calor numulariis
• V gradus, et maxima fabrica titanium offensionibus. Qua re admodum magno robore. princeps calor resistentiam.
• VII gradus, superior et MORSUS reducere corrosio resistentiam in ambitum mutandum.
• IX gradus, Ipsum excelsum vires et corrosio resistentiam.
• XII gradus: Potius quam pura calor resistentia Titanium. Part VII: et applications ut Romani XI.
• XXIII gradus: Titanium 6Aluminum, ELI, 4Vanadium (Extra Minimum Interstitial) Alloy applicationem ad INSTITUO manu.