15-5pH mixturae ferro lentitiem est quam 17-4 disposito habere maiorem PH. In addition 15-5 martensitic est in structuram et adhuc in annealed valetudo confirmat inductio aeris sit relative humilis temperatus calor curatio, quae continet tempus praecipitat in admisceri genus. XII, XIII 15-5 is quoque relatum ut ut in quibusdam cubits
C |
cr |
NI |
si |
mn |
P |
S |
Cu |
Mo |
≤0.07 |
14.0-15.5 |
3.5-5.5 |
≤1.0 |
≤1.0 |
≤0.04 |
≤0.03 |
2.5-4.5 |
0.15-0.45 |
CRASSITUDO |
Electric resistivity |
Calor facultatem specifica |
Expansion scelerisque coefficiens |
7,8 |
0.98 |
460 |
10,8 |
conditione, |
бb / N / mm2 |
б0.2 / N / mm2 |
δ5 /% |
ψ |
HRC |
|
praecipitatio |
CDLXXX ℃ miscueratque |
1310 |
1180 |
10 |
35 |
≥40 |
DL ℃ miscueratque |
1070 |
1000 |
12 |
45 |
≥35 |
|
DLXXX ℃ miscueratque |
1000 |
865 |
13 |
45 |
≥31 |
|
DCXX ℃ miscueratque |
930 |
725 |
16 |
50 |
≥28 |
AMS (V)DCLIX, AMS (V)DCCCLXII, ASTM-A564 (-XII XIII), 7-240 BMS (Boeing), W. 1,4545 Nr./EN
• Die Hardening
• alta virtus:
• Moderatus corrosio resistentia ad DC ° F
• aerospace applications
• Et eget petrochemical applications
• Chartam et pulpam
• cibum processui