Est C2000 Hastelloy novum genus Cr-Mo-Ni, admisceri genus. Ex C4 mixturae, in contentus de interdum est melius et etiam amplio oxidatio et aeris magno corrosio resistentia et facultatem ad medium inclusos redacturum, admisceri genus. Hastelloy C2000 sit amet serie alloys et corrosio resistentiam H2SO4 bonum, sed quod bonum est resistendum corrosione intercrystalline mixturae C4
alloy | C | cr | NI | Fe | Mo. | W | Cu | si | mn | P | S |
C-MM Hastelloy | ≤0.01 | 22.0-23.0 | statera | ≤3.0 | 15.0-17.0 | 3.0-4.5 | 1.3-1.9 | ≤0.08 | ≤0.5 | ≤0.02 | ≤0.08 |
CRASSITUDO
|
8.5 g / cm
|
Liquescens punctum
|
℃ 1260-1320
|
crassitudine (Mm) |
Tensile vires (Mpa) | Cedat imperium σ0.2 (Mpa) |
elongation (50.8mm) (%) |
1.6 | 752 | 358 | 64.0 |
3,18 | 765 | 393 | 63.0 |
6,35 | 779 | 379 | 62.0 |
12,7 | 758 | 345 | 68.0 |
25,4 | 752 | 372 | 63.0 |
ASTM B564, ASTM B574, ASTM B575, ASTM B619, ASTM B622, ASTM B366
Bar / Virga | filum | Habena / spiram | Sheet / Plate | Pipe / Tube |
SULPHURATUS acidum corrosio resistentiam inter hydrofluoric hydrochloric acid phosphate organicum CHLORUM metallum intromitti rimulam corrosio alcali pitting, pede accentus fractura.
Mixturae C-MM ostendit melius pateat rima, et pitting resistentia ad corrosio est CCLXXVI mixturae C-vexillum est industriae.
Et ex Vicifontem machining formability Hastelloy C MM C276 similes sunt, ab offensionibus consilium dubitationem solvere.
Optimum amet pede renititur quin hac reductione ad metallicam vertuntur tandem coniunctim afficient vniuersa magna interdum et molybdenum aeris et contenta.
• reactor In chemical industria processus, calor exchanger: columnas et organo.
• De pharmaceutical industria et reactor dryer.
• LANUGO Gas desulfurization ratio.