IV humilis-carbo carbonis C Hastelloyc est austenitic interdum molybdenum, nickel, admisceri genus.
IV, prima et principalis differentia HastelloyC chemica compositio similis admixtos humilitatem ipsum diam, ferrosilicate et tungsten contentus.
Tales autem facit compositionem ostendere optimum eget status apud 650-1040 ℃, emendare facultatem resistere intergranular ærugo, in conditionibus potest vitare oportet vestibulum pede ore rectam sentiendi et aestus per pactionem zona corrosio.
alloy |
% |
Fe |
cr |
NI |
Mo. |
co |
C |
mn |
si |
S |
P |
W |
V |
Hastelloy C-IV |
Min. |
- |
14.0 |
statera |
14.0 | - | - | - | - | - | - |
2.5 |
- |
Max. |
3.0 |
18.0 |
17.0 |
2.0 | 0.015 | 3.0 | 0,1 | 0.01 | 0,03 | 3.5 | 0,2 |
CRASSITUDO
|
8-94 g / cm
|
Liquescens punctum
|
℃ 1325-1370
|
Status
|
Distrahentes fortitudo
Rom N / mm² |
Cedat imperium
2N 0, R / mm² |
elongation
sicut% |
Brinell duritiam incantatorum
Versus Res
|
Solutio in curatio
|
690
|
276
|
40
|
-
|
Bar / Virga | Habena / spiram | Sheet / Plate | Pipe / Tube | Forgings |
B335 ASTM | B333 ASTM | ASTM B622, ASTM B619, ASTM B626 | B564 ASTM |
• Corrosio resistentiam habet optimum maxime corrosivis media praecipue in reducta conditio.
• Corrosio resistentiam in optimum loci Halides.
• LANUGO Gas ratio desulfurization
• Acidum regenerationem plantis lutosa,
• Et acetic acidum productio agro-chemical
• Titanium dioxide productio (CHLORUM modum)
• electroplating