Admisce 46 UNS K94600 talea / sheet/ habena

Product Detail

Communes Trade Names: Admisce 46, 4J46, Fe-46Ni, UNS K94600, NiLo46

Admisceamus 46 in dato termino peractum obtinetur componendo contentum energiae internae nickel et expansionem coefficiens diversarum softglass et ceramicae congruentem seriem emissionis mixturae, dilatationis coefficientis et temperaturae Curie cum augmento nickel contentorum. late in electrico vacui industria adhibita structuram signandi materiae e.

Admisce 46 Chemical Compositio

Ni	Fe	C	Cr	P	Si	Co	Mn	Al	S
45.0~47.0	Bal	≤0.05	≤0.025	≤0.02	≤0.3	-	≤0.80	≤0.10	≤0.02

Admisce 46Basic physica constantes et Mechanica Properties

Brand	Scelerisque conductivity	Imprimis calor facultatem	Density	Punctum liquescens (℃)	Electric resistivity	Curie punctum
Admisce 46	14.7	502J	8.18	1427	0.49	420

Admisce 46 coefficiens expansionis linearis

Gradus	Curatio caloris exempla	Mediocris expansion coefficiens linearibus
Gradus	Curatio caloris exempla	20~300°C	20~400°C	20~500°C
Admisce 46	Calefacere ad 850~900°C in atmosphaera defensiva vel in statu vacuo, habe per horam 1 et tunc refrigerabis ad 300℃ ad minus quam 300℃/h.	5.5~6.5	5.6~6.6	7.0~8.0

Notae:
1. Vickers duritiem habenae annatae non plus quam 170 esse debent.
2. Pro liberata detractione, postquam calor in 900℃ tractatur, et tunc pro 30 min obtinebit, durities Vickerorum non plus quam 170 esse debet.

Admisce 46 coefficiens expansionis linearis

Gradus	Mediocris coefficiens expansionis linearis in diversis temperaturis, ā/(10-6/K)
Admisce 46	20~100℃	20~200℃	20~300℃	20~400℃	20~500℃	20~600℃
Admisce 46	6.8	6.5	6.4	6.4	7.9	9.3

Admisce 46 Mechanica Property

Gradus	Curatio caloris temperatus, ℃	Robur distrahens, si/MPa	Tractus distrahens, δ(%)	Vickers duritia	Frumenti magnitudine
Admisce 46	750	527.5	34.8	137.4	7
	850	510	35.4	134.6	6
	950	483.5	36.7	128.1	6~5
	1050	466.5	34.3	125.6	5~4